Aluminum　alloy　3003　is　studied　after　isothermal　compression　in　a　Gleeble-1500　machine　at　a　rate　of　0.01　-　10　sec　(-　1)　in　the　temperature　range　of　300　-　500A　degrees　C.　The　curves　plotted　in　the　coordinates　＂strain　hardening　rate　-　strain＂　are　used　to　determine　the　critical　strain　epsilon(c)　and　the　static　strain　epsilon(s)　for　dynamic　recrystallization,　and　the　curve　of　the　dynamic　recrystallization　is　plotted.　A　mathematical　model　describing　the　kinetics　of　the　dynamic　recrystallization　as　a　function　of　the　treatment　parameters　is　suggested.