Two　zinc　arsonate　coordination　polymers,　Zn(4-apa)center　dot　H2O　(1,　4-apaH(2)　=　4-aminophenylarsonatic　acid)　and　Zn(4-apa)　(2),　have　been　hydrothermally　synthesized　and　characterized　by　elemental　analysis,　IR　and　single-crystal　and　powder　X-ray　diffraction.　Crystal　data　for　1:　monoclinic,　space　group　C2/c　with　a　=　23.056(5),　b　=　5.4224(11),　c　=　15.027(3)　angstrom,　beta　=　121.22(3)degrees,　V　=　1606.6(6)　angstrom(3),　D-c　=　2.468　g.cm(-3),　F(000)　=　1168,　mu　=　7.122　mm(-1),　Z　=　8,　the　final　R　=　0.0309　and　wR　=　0.0752　for　1763　observed　reflections　with　I　＞　2　sigma(I).　For　2:　monoclinic,　space　group　P2(1)/c　with　a　=　8.7852(18),　b　=　9.2744(19),　c　=　9.752(2)　angstrom,　beta　=103.45(3)degrees,　V　=　772.7(3)　angstrom(3),　D-c　=　2.410　g.cm(-3),　F(000)　=　544,　mu　=　7.387　mm(-1),　Z　=　4,　the　final　R　=　0.0321　and　wR　=　0.0741　for　1696　observed　reflections　with　I　＞　2　sigma(I).　The　structure　of　1　shows　a　two-dimensional　(4,4)-network　composed　of　an　inorganic　ladder　chain　bridged　by　the　phenyl-linkers　of　4-apa　ligands.　Compound　2　exhibits　a　3D　layer-pillared　framework　with　crb　net,　in　which　inorganic　(4.8(2))-networks　are　joined　by　the　phenyl-linkers.