Co-doped　TiO2　crystals　(Co:TiO2)　were　grown　by　Czochralski　growth　(CZ)　method　and　the　edge-defined　film-fed　growth　(EFG)　method,　respectively.　Therein,　EFG　was　an　effective　method　to　grow　a　higher　quality　Co:TiO2　crystal　without　the　reverse　flow　of　the　melt.　This　as-grown　crystal　reaches　a　larger　dimension　of　10　mm　x　15　mm　x　18　mm.　XRD　analysis　confirms　that　as-grown　crystal　is　isostructural　with　TiO2　rutile　phase.　Moreover,　this　crystal　has　ferromagnetism　at　room　temperature　and　the　magnetic　moment　of　Co　ion　is　1.25　x　10(-2)mu(B)/Co.　After　annealed　at　1273　K,　Co.TiO2　crystal　enhances　obviously　its　optical　transmittance,　while　this　crystal　shows　diamagnetism　due　to　the　disappearance　of　the　ferromagnetic　signal.