Nanocrystals　of　Ce1-xMnxO2-delta　(x　=　0.00,　0.05,　0.10,　0.15,　and　0.20)　were　synthesized　by　a　hydrothermal　reaction　route.　The　solid　solutions　crystallized　in　a　cubic　fluorite　structure　with　a　particle　size　in　the　range　of　11　similar　to　15　nm.　The　incorporation　of　Mn　ions　in　CeO2　resulted　in　a　lattice　volume　reduction.　Mn　ions　showed　a　mixed　valence　state　of　+2,　+3　and　+4　in　CeO2　lattice.　An　obvious　red-shift　of　the　absorption　threshold　edge　was　observed　from　the　UV-visible　spectrum;　Compared　with　the　bulk　CeO2,　Ce1-xMnxO2-delta　nanocrystals　exhibited　a　lower　releasing　oxygen　temperature　as　indicated　by　TPR　technique.