Pluronic　F68　is　a　poly　(ethylene　oxide)　-　poly　(propylene　oxide)　-　poly　(ethylene　oxide)　triblock　copolymer　(indicated　as　(EO)　x　-　(PO)　y　-　(EO)　x　with　x　=　76　and　y　=　29).　Experimental　results　showed　that　F68　formed　micelle　at　50　°C.　The　micellar　core　consisted　of　80%　PO　and　20%　EO　components.　The　hydrophilic　PEO　blocks　extended　into　the　surrounding　aqueous　solvent,　forming　a　＂corona＂　around　the　core.　The　intrinsic　viscosity　of　F68　micelle　at　50　°C　was　determined　to　be　11.6　cm3　·　g-1　and　the　weight　of　hydrating　water　per　g　of　solute　was　3.6　g.　Solubilization　of　naphthalene,　anthracene　and　pyrene　in　F68　aqueous　micellar　solutions　at　50　°C　was　investigated　by　UV　-　spectra　measurements.　The　results　showed　that　the　partition　coefficients　(Kv)　of　naphthalene,　anthracene　and　pyrene　between　the　micelle　and　water　were　2.54　×　102,　7.94　×　102　and　8.74　×　102　respectively.