The　microstructure,　precipitation　hardening　and　magnetic　properties　of　melt-spun　Fe78Co11Mo11　and　Fe74Co11Mo11B4　alloys　were　studied.　It　is　shown　that　B　addition　increases　the　precipitation　reaction　temperature　of　the　supersaturated　matrix　from　605　°C　for　the　Fe78Co11Mo11　alloy　to　640　°C　for　the　Fe74Co11Mo11B4　alloy.　In　the　Fe78Co11Mo11　alloy,　a　cotton-shaped　(Fe,Co)7Mo6　precipitate　is　observed　inside　the　grains　of　the　matrix　phase.　In　the　Fe74Co11Mo11B4　alloy,　in　addition　to　the　(Fe,Co)7Mo6　phase,　spherical　MoB2　precipitates　are　also　observed.　Compared　to　the　Fe78Co11Mo11　sample,　the　Fe74Co11Mo11B4　sample　exhibits　a　finer　and　more　homogeneous　microstructure　with　more　equiaxed　grains.　This　finer　microstructure　explains　the　enhanced　hard　magnetic　properties　in　the　Fe74Co11Mo11B4　sample　(Mr　=　60.4　A　m2/kg,　iHc　=　20.8　kA/m)　compared　to　those　of　the　Fe78Co11Mo11　sample　(Mr　=　56.5　A　m2/kg,　iHc　=　17.3　kA/m).　Furthermore,　the　Fe74Co11Mo11B4　sample　shows　better　antioxidant　ability　than　the　Fe78Co11Mo11　sample,　especially　when　the　temperature　exceeds　400　°C.　©　2018　Elsevier　B.V.