La　doped　BaTiO3　(LBT)　material　was　prepared　by　sol-gel　method.　The　effect　of　La-doping　content　on　the　electrical　performance　of　BaTiO3　material　was　studied　by　X-ray　diffraction,　scanning　electron　microscopy　and　conductivity.　The　results　show　that　the　single-phase　perovskite　structure　of　LaxBa1-xTiO3　(x=0-0.4)　powder　can　be　obtained　after　calcined　at　900℃.　The　conductivity　of　BaTiO3　Improved　obviously　by　La-doping.　When　x=0.2,　the　La0.2Ba0.8TiO3　(LBT20)　material　exhibits　excellent　chemical　compatibility　with　Gd　doped　ceria　Ce0.8Gd0.2O1.9　electyolyte　material,　and　LBT20　shows　the　highest　conductivity,　up　to　approximately　0.15　S/cm　at　800℃　under　the　reducing　atmosphere,　which　is　four　times　higher　than　that　of　BT　tested　under　the　same　condition.　These　results　indicate　that　the　LBT20　can　be　considered　as　potential　anode　materials　for　IT-SOFC　operating　on　hydrocarbon　fuels　directly,　but　its　conductivity　needs　to　be　further　improved.　©,　2015,　Rengong　Jingti　Xuebao/Journal　of　Synthetic　Crystals.　All　right　reserved.