A　pyrochlore　crystal　with　magneto-optical　effect　-　Ho2Ti　2O7　crystal　has　been　grown　by　Czochralski　method.　X-ray　powder　diffraction,　magnetic　susceptibility,　transmission　spectrum　and　Faraday　rotation　of　single　crystal　Ho2Ti2O7　were　measured.　The　results　of　Rietveld　refinement　revealed　that　the　crystal　belongs　to　cubic　system　and　the　lattice　parameters　calculated　by　Jade　7.0　(Materials　Data,　Inc.)　were　a=1.00915(7)　nm　and　V=1.0277　nm3.　The　effective　magnetic　moment　and　Curie-Weiss　temperature　of　Ho2Ti　2O7　crystal　are　10.4　μB　and　1.86　K,　respectively.　The　transmittance　of　Ho2Ti2O7　crystals　grown　in　Ar　can　be　more　than　72%　in　700-1080　nm　and　1260-1500　nm.　The　Verdet　constant　of　Ho2Ti2O7　crystal　at　1064　nm　comes　up　to　-54.1　rad/(mT),　which　is　1.35　times　as　large　as　that　of　Tb　3Ga5O12　reported.　©　2014　Published　by　Elsevier　B.V.