Melamine-modified　lignin(MEHL)was　prepared　using　grafting　reaction　from　hydrolyzed　lignin(EHL)by　enzyme,　melamine　and　formaldehyde,　and　its　adsorption　for　silver　ions　was　studied.　The　results　from　grafting　reaction　showed　that　content　of　melamine　and　formaldehyde　had　great　influences　on　MEHL　yield.　High　yield　83.7%　for　MEHL　was　achieved　with　EHL:　melamine:　formaldehyde　mass　ratio　10:　6:　6　at　reaction　temperature　90°C　and　reaction　time　4　h.　The　MEHL　obtained　was　characterized　by　FTIR,　TGA　and　elemental　analysis.　The　results　showed　that　melamine　molecules　had　been　grafted　onto　EHL　chains.　Nitrogen　content　in　MEHL　had　obvious　increase　from　original　0.81%　to　18.55%.　Furthermore,　the　adsorption　performance　for　silver　ions　at　the　same　conditions　was　much　stronger　for　MEHL　than　for　EHL.　Its　maximum　adsorption　capacity　was　up　to　944.1　mg·g-1　at　optimal　conditions:　50　mg　MEHL,　initial　silver　ion　concentration　0.16　mol·L-1,　30°C　and　36　h.　©　All　Rights　Reserved.