A　CeO　2-ZrO　2-Al　2O　3　composite　oxide　(CZA)　and　a　CeO　2-ZrO　2　composite　oxide　(CZ)　were　prepared　by　the　co-precipitation　method.　The　samples　were　thermally　aged　in　a　flowing　air　atmosphere　and　in　10%　H　2/Ar　flow.　The　structure　and　performance　of　the　composite　oxides　were　studied　by　X-ray　diffraction　(XRD),　oxygen　storage　capacity　(OSC)　measurements,　and　H　2　temperature-programmed　reduction　(H2-TPR).　The　results　show　that　a　CeAlO　3　phase　was　formed　after　CZA　was　reductively　aged　at　950　°C　and　an　increase　in　temperature　benefited　the　formation　of　CeAlO　3.　The　OSC　of　CZA　increased　with　an　increase　in　the　reductive　treatment　temperature　and　it　was　1270.3　μmol·g　-1　when　the　temperature　reached　900　°C.　However,　the　OSC　decreased　with　an　increase　in　the　temperature.　After　CZA　was　reduced　at　1100　°C　the　OSC　was　only　23.2　μmol·g　-1.　We　found　that　the　OSC　and　the　reducibility　of　the　material　were　remarkably　influenced　by　the　formation　of　a　CeAlO　3　phase　after　CZA　was　reductively　aged.　©　Editorial　office　of　Acta　Physico-Chimica　Sinica.