Yb0.140　Gd0.813La0.047VO4　crystal　was　grown　by　the　Czochralski　method.　The　effective　segregation　coefficients　of　Yb3+　and　La3+　ions　in　crystal　are　0.　80　and　0.　47,　respectively.　The　doping　ion　of　La3+　can　improve　the　laser　damage　threshold　and　the　stability　of　crystal-growth　process　of　Yb:　GdVO4　crystal,　weaken　the　fluorescence　quenching　and　the　fluorescence　trapping　effects　of　high　Yb3+-doped　crystals.　The　crystal　has　large　the　full　widths　at　half　maximum　(FWHM)　of　the　absorption　and　fluorescence　spectra,　which　is　26nm　and　47nm,　respectively,　and　the　large　absorption　cross　section　and　emission　cross　section　that　is　2.26　×　10-20　cm2　and　0.　96　×　10-20　cm2,　respectively.　So　Yb0.140Gd0.813La0.047VO4　crystal　may　be　applicable　for　femtosecond　laser　and　for　the　tunable　laser.