Sensing　temperature　(T)　has　gained　great　attention　since　T　is　the　most　important　parameter　in　daily　life,　scientific　research　and　industry.　A　ratiometric　fluorescence　T　sensor　is　fabricated　by　doping　MAPbBr(3)　perovskite　nanocrystals　(PNCs)　and　rhodamine　B　(RhB)　into　a　polyacrylonitrile　(PAN)　matrix　and　the　composite　materials　are　electrospun　into　optical　fibers.　The　fibers　show　characteristic　emissions　at　521　and　587　nm　under　UV　irradiation　(lambda(ex)　=　365　nm).　Both　emission　intensities　gradually　increased　with　elevating　T,　accompanied　with　a　fluorescence　color　change　from　green　to　yellow.　There　is　a　linear　relationship　between　fluorescence　intensity　ratio　(I-521/I-587)　and　T　in　the　range　of　30-45　degrees　C.　The　T　response　sensitivity　is　as　high　as　4.38%　degrees　C-1　at　45　degrees　C.