Two　new　silver-iron　based　phosphates　AgFe2(PO4)2F(H2O)2　(1)　with　monoclinic　P21/n　and　Ag3Fe2(PO4)(HPO4)3　(2)　with　triclinic　P-1　were　synthesized　by　a　conventional　hydrothermal　method,　featuring　a　dimer　structure　and　a　twisted　honeycomb-like　lattice,　respectively.　XPS　and　BVS　(Bond　Valence　Sum)　calculations　indicated　only　Fe3+　ions　in　both　compounds,　while　FT-IR　spectra　proved　the　presence　of　[H2O]　in　1　and　[OH]　groups　in　2.　Solid-state　UV-vis-NIR　diffuse　reflectance　spectra　suggested　their　wide　optical　band　gaps　of　2.31　eV　and　1.94　eV,　respectively.　Magnetic　measurements　indicated　that　both　compounds　display　a　long-range　antiferromagnetic　ordering　at　low　temperature,　showing　the　change　of　magnetic　entropy　of　9.59　J　mol-1　K-1　in　1　and　that　of　14.87　J　mol-1　K-1　in　2,　respectively.