A　pyrochlore　crystal　with　magneto-optical　effect　-　Dy2Ti2O7　crystal　with　19-20　mm　in　diameter　and　21　mm　in　length　has　been　grown　by　the　Czochralski　method.　The　lattice　parameters　were　calculated　by　X-ray　powder　diffraction,　which　revealed　that　the　crystal　belongs　to　cubic　system.　Absorption　spectrum　was　measured　in　the　visible　and　near-infrared　region　at　room　temperature,　which　indicated　the　crystal　has　low　absorption　coefficient　at　600-760　nm.　The　specific　Faraday　rotation　of　single　crystal　was　measured　at　room　temperature　in　532,　633,　and　1064　nm.　The　Verdet　constant　of　Dy2Ti2O7　crystal　at　633　nm　comes　up　to　183　rad/(m　T),　which　is　as　1.4　times　as　that　of　TGG　reported.　(C)　2014　Elsevier　B.V.　All　rights　reserved.