The　Yb3+:Ca9Gd(VO4)7　crystal　with　dimensions　of　Φ19　×　25　mm3　was　grown　by　the　Czochralski　method　for　the　first　time.　The　polycrystalline　materials,　crystal　growth,　absorption　and　fluorescence　spectra,　energy　level　schema,　fluorescence　lifetime　and　laser　performance　parameters　were　investigated　in　detail.　For　π-polarization,　the　absorption　coefficients,　cross-sections,　maximal　full　width　at　half　maximum　(FWHM)　at　around　976　nm　are　1.05　cm−1,　1.27　×　10−20　cm2　and　33　nm,　respectively.　For　σ-polarization,　the　relevant　absorption　spectral　parameters　at　around　981　nm　are　1.58　cm−1,　1.90　×　10−20　cm2　and　28　nm,　respectively.　At　the　laser　wavelength　around　1023　nm,　the　FWHM　and　emission　cross-sections　are　57　nm　and　0.94　×　10−20　cm2　for　π-polarization,　54　nm　and　2.18　×　10−20　cm2　for　σ-polarization,　respectively.　The　results　reveal　that　Yb3+:Ca9Gd(VO4)7　crystal　can　be　regarded　as　a　potential　candidate　for　efficient　LD-pumping　and　ultrashort　pulse　laser　crystal.　©　2020　Elsevier　B.V.