A　sodium　terbium　molybdate　(NaTb(MoO4)2)　single　crystal　with　dimensions　of　∅　20　mm25　mm　was　grown　by　the　Czochralski　method.　The　lattice　parameters　of　the　crystal　were　determined　by　XRD　analysis.　The　absorption　spectrum　and　Faraday　rotation　spectrum　(B=1.07　T)　were　investigated　at　wavelengths　of　400-1500　nm　at　room　temperature.　The　Verdet　constants　of　NaTb(MoO4)2　crystal　were　measured　at　532,　633　and　1064　nm　wavelengths　by　the　extinction　method.　The　results　show　that　NaTb(MoO4)2　has　a　larger　magneto-optical　figure　of　merit　than　that　of　TGG　at　wavelengths　of　660-1500　nm.　©　2008　Elsevier　B.V.　All　rights　reserved.