This　paper　reports　the　crystal　growth　and　spectral　properties　of　Nd　3+:Sr2La0.667(VO4)2　crystals.　Nd:Sr2La0.667(VO4)2　crystal　with　dimension　20×15×15　mm3　was　grown　by　the　Czochralski　method.　The　segregation　coefficients　of　Nd3+　in　Nd　3+:Sr2La0.667(VO4)2　crystal　is　0.52.　The　hardness　of　Nd3+:Sr2La　0.667(VO4)2　crystal　is　374.6　VDH,　and　is　about　equal　to　5.0　moh.　Nd:Sr2La0.667(VO4)　2　crystal　has　a　large　FWHM　of　21　nm　at　810　nm.　The　absorption　and　emission　cross-sections　were　2.6×10-20　cm2　at　810　nm　and　16.4×10-20　cm2　at　1079　nm,　respectively.　©　2005　Elsevier　B.V.　All　rights　reserved.