This　paper　reports　the　crystal　growth　and　spectral　properties　of　Nd3+:Sr2La0.667(VO4)(2)　crystals.　Nd:Sr2La0.667(VO4)(2)　crystal　with　dimension　20　x　15　x　15　mm(3)　was　grown　by　the　Czochralski　method.　The　segregation　coefficients　of　Nd3+　in　Nd3+:Sr2La0.667(VO4)(2)　crystal　is　0.52.　The　hardness　of　Nd3+:Sr2La0.667(VO4)(2)　crystal　is　374.6　VDH,　and　is　about　equal　to　5.0　moh.　Nd:Sr2La0.667(VO4)(2)　crystal　has　a　large　FWHM　of　21　nm　at　810　nm.　The　absorption　and　emission　cross-sections　were　2.6　x　10(-20)　cm(2)　at　810nm　and　16.4　x　10(-20)　cm(2)　at　1079　nm,　respectively.　(c)　2005　Elsevier　B.V.　All　rights　reserved.