The　microstructure,　precipitation　hardening　and　magnetic　properties　of　melt-spun　Fe78Co11Mo11　and　Fe74Co11Mo11B4　alloys　were　studied.　It　is　shown　that　B　addition　increases　the　precipitation　reaction　temperature　of　the　supersaturated　matrix　from　605　degrees　C　for　the　Fe78Co11Mo11　alloy　to　640　degrees　C　for　the　Fe74Co11Mo11B4　alloy.　In　the　Fe78Co11Mo11　alloy,　a　cotton-shaped　(Fe,　Co)(7)Mo-6　precipitate　is　observed　inside　the　grains　of　the　matrix　phase.　In　the　Fe74Co11Mo11B4　alloy,　in　addition　to　the　(Fe,　Co)(7)Mo-6　phase,　spherical　MoB2　precipitates　are　also　observed.　Compared　to　the　Fe78Co11Mo11　sample,　the　Fe74Co11Mo11B4　sample　exhibits　a　finer　and　more　homogeneous　microstructure　with　more　equiaxed　grains.　This　finer　microstructure　explains　the　enhanced　hard　magnetic　properties　in　the　Fe74Co11Mo11B4　sample　(M-r　=　60.4　Am-2/kg,　H-i(c)　=　20.8　kA/m)　compared　to　those　of　the　Fe78Co11Mo11　sample　(M-r　=　56.5　Am-2/kg,　H-i(c)　=　17.3　kA/m).　Furthermore,　the　Fe74Co11Mo11B4　sample　shows　better　antioxidant　ability　than　the　Fe78Co11Mo11　sample,　especially　when　the　temperature　exceeds　400　degrees　C.　(C)　2018　Elsevier　B.V.　All　rights　reserved.