This　paper　reported　the　crystal　growth　and　spectroscopy　characters　of　Cr3+:Li2Mg2(MoO4)(3).　The　refractive　index　of　Cr3+:Li2Mg2(MoO4)(3)　crystal　is　1.87　and　the　hardness　is　270　HV.　This　crystal　shows　broadband　absorption　property　with　peak　wavelength　at　about　495　and　699　nm.　The　absorption　crosssection　is　14.75　x　10(-20)　cm(2)　at　495　nm　and　9.63　x　10-20　cm2　at　699　nm,　respectively.　The　crystal　field　strength　and　energy　levels　of　Cr3+　ion　were　calculated　based　on　the　spectroscopic　data.　The　Cr-3　:Li2Mg2(MoO4)(3)　crystal　shows　broadband　emission　extending　from　750　to　1300　nm　even　excited　at　10　K.　The　room　temperature　emission　cross　section　is　72x10(-2)　cm(2)　at　926　nm.　A　discussion　of　the　relation　between　the　spectroscopic　properties　and　crystal　field　parameters　of　Cr3+:Li2Mg2(MoO4)(3)　crystal　was　presented　based　on　the　solid　state　spectroscopy　theory.