BiFeO3-Pb(Mg1/3Nb2/3)O-3-PbTiO3　(BF-PMN-PT)　ternary　ceramics　with　pure　perovskite　phase　were　prepared　through　a　two-step　solid　reaction　method.　Based　on　structural　analysis,　the　ternary　phase　diagram　of　BF-PMN-PT　solid　solution　at　room　temperature　has　been　established.　The　Curie　temperature　T-C,　remnant　polarization　P-r　and　piezoelectric　constant　d(33)　vary　in　the　range　of　138　to　225　A　degrees　C,　15.12　to　23.65　mu　C/cm(2)　and　129　to　276　pC/N,　respectively.　The　coercive　field　Ec　increases　gradually　from　5.77　to　29.56　kV/cm　upon　PT　content　increasing.　The　magnetic　study　suggests　that　the　magnetism　turns　from　diamagnetism　for　PMN-PT　to　paramagnetism　for　BF-PMN-PT　by　adding　BiFeO3　into　PMN-PT　and　adding　more　content　of　BF　does　not　change　the　paramagnetism　further.